Tapes - Skived and Rolls

 

 

ABS-
ACETAL (POM)
ACRYLIC (PMMA)
Carbon Fiber
Cellulose Acetate and Butyrate
CPVC

ETFE
EVA
Films
FIBERGLASS FRP
Fluorpolymers

Fluorosint®

 

Graphite
HDPE (High Density Polyethylene)
Hytrel Sheets®

Kapton®

 
Kevlar®
KYDEX®  FR Sheets
Laminates - Phenolics -Micarta  
LDPE (Low Density Polyethylene)
MDPE (Medium Density Polyethylene)
Mylar® 
Neoprene® 
Nomex Film®
Norprene®
Noryl®
Nylon
PBI
PBT
PCTFE
Peek
PetG - PetP
PES Plastic Sheet

PFA
Polycarbonate
Polyester
Polyimide-Vespel, Cirlex, Pyropel 
Polypropylene
Polystyrene (HIPS)
Polysulfone
Polyurethane

 
PPS
PVC
PVDF
Rubber
Santoprene TPE
Silicone
Sintimid 
TEFLON®  

Torlon
TPX Films
Tygon Tubing

 
UHMWPE
Ultem

Texas Longhorns

Contact Kmac Plastics

Privacy

 

Domestic Selling Policy

Square Watermelon Cases

Tube Caps & Plugs

 

 

CHEMICALS

Acids
Side by Side Material Comparison Chemical Resistance Chart (Note: Large File)

 

Reagent Time Exposed Percent Increase Observed Condition of Plastic
Weight Thickness
 Acetic, 5% 1 year 3.6 2.1 Slightly softened
 Acetic, 10% 2 months 5.2 2.4 Slightly softened
•Acetic, 30% 2 months 13.6 8.6 Softened and swollen
 Boric, 5% 2 days 1.3 0.0 Unchanged
 Chromic, 6% 8 days
(38ºC, 100ºF)		 2.0 0.1 Slightly stained
 Citric, 10% 4 months
(60ºC, 140ºF)		 1.6 0.8 Slightly softened
 Citric, 10% 1 year 1.4 0.6 Unchanged
•Citric, 60% 4 months
(60ºC, 140ºF)		 — — Surface attacked
 Fluosilicic,
 10%		 2 months 4.5 1.2 Unchanged
 Fluosilicic,
 28%		 2 months 4.7 3.6 Unchanged
 Formic, 3% 20 days — — Unchanged
 Hydrochloric,
 10%		 1 year 0.9 0.5 Surface slightly attacked
•Hydrofluoric,
 10%		 1 month 10.3 5.5 Slightly swollen and softened
•Hydrofluoric,
 48%		   — — Dissolved
 Lactic, 50% 2 days 1.6 0.5 Unchanged
•Nitric, 10% 8 months — — Decomposed
 Oleic 1 year 2.3 1.5 Unchanged
 Phosphoric,
 30%		 2 months 1.3 0.8 Unchanged
 Phosphoric,
 50%		 2 months 1.6 0.8 Unchanged
•Phosphoric,
 75%		 2 months — — Partially decomposed
 Pyrogallic,
 4%		 1 week 2.6 1.1 Stained yellow
 Stearic 1 week — — Unchanged
 Sulfuric, 3% 1 year 1.6 1.0 Slightly discolored
 Sulfuric, 10% 1 year 1.5 0.7 Slightly discolored
•Sulfuric, 20% 1 year 0.9 0.3 Slightly softened, surface attacked
•Sulfuric, 30% 1 year –0.4 –0.3 Surface attacked
•Sulfuric, 94%   — — Disintegrated
 Tannic, 10% 4 months
(38ºC, 100ºF)		 2.8 1.2 Unchanged
 Trichloroacetic,
 1%		 1 month 3.3 0.5 Unchanged
•Trichloroacetic,
 5%		 1 month 9.3 3.1 Softened



Alcohols, Monohydric

Reagent Time Exposed Percent Increase Observed Condition of Plastic
Weight Thickness
 n-Amyl 2 days 3.1 3.0 Unchanged
•tert-Amyl 2 days 14.0 11.3 Softened, tacky
•n-Butyl 2 days 6.5 7.2 Swollen
•sec-Butyl 2 days 7.2 10.7 Swollen
•tert-Butyl 2 days 3.6 3.3 Slightly softened
•Diacetone   — — Dissolved
•Ethyl (denatured) 2 days 23.0 24.7 Softened
•Ethyl, 50% 1 week 13.4 11.6 Softened
•2-Ethylhexyl 1 week — — Swollen
•Isoamyl 2 days 2.0 2.1 Very slightly softened
•Isopropyl 2 days 23.4 25.1 Softened, tacky
•Methyl   — — Dissolved
 Methyl, 5% 1 year 2.0 1.2 Slightly softened
•n-Propyl 2 days 15.0 4.4 Slightly softened
•Tetrahydrofurfuryl   — — Dissolved

Alcohols, Dihydric and Trihydric

Reagent Time Exposed Percent Increase Observed Condition of Plastic
Weight Thickness
•Diethylene
 Glycol		 2 months 8.2 6.1 Softened
 2-Ethyl
 Hexanediol-1,3		 2 days
(38ºC, 100ºF)		 — — Unchanged
 Ethylene
 Glycol		 1 year 4.2 2.1 Unchanged
 Glycerin 1 year 0.0 0.4 Unchanged
 Propylene
 Glycol		 2 days 0.4 0.0 Unchanged
•Triethylene
 Glycol		 2 months 8.6 6.7 Softened

Hydrocarbons

Reagent Time Exposed Percent Increase Observed Condition of Plastic
Weight Thickness
 Gas, Natural,
 aromatic-free		 1 year — — Showed slight decrease in tensile strength and increase in impact strength
 Gas, Natural,
 5% aromatic
 content		 23 days — — Showed slight decrease in tensile strength and increase in impact strength
 Heptane 1 year 1.6 2.5 Unchanged
 Hexane 1 week — — Unchanged
 Propane, gas 2 months 0.3 0.6 Unchanged
 Propane, liquid 2 months 1.4 4.6 Unchanged
•Toluene 2 days 39.3 54.9 Softened
•Xylene 1 week 41.5 33.2 Softened




Hydrocarbons, Halogenated

Reagent Time Exposed Percent Increase Observed Condition of Plastic
Weight Thickness
•Carbon Tetrachloride 2 days 14.8 6.8 Surface slightly softened
•Chlorobenzene   — — Dissolved
•Chlorobromomethane   — — Dissolved
•Chloroform   — — Dissolved
•o-Dichlorobenzene 3 days — — Softened and swollen
•p-Dichlorobenzene 3 days 11.1 11.7 Swollen
•Ethylene Chloride   — — Dissolved
•Methylene Chloride   — — Dissolved
•Propylene Chloride   — — Dissolved
•s-Tetrabromoethane 3 days — — Softened, swollen, and tacky
•Tetrachloroethane   — — Dissolved
•Tetrachloroethylene 12 days — — Badly swollen
•Trichloroethylene 1 day — — Badly swollen




Ketones

Reagent Time Exposed Percent Increase Observed Condition of Plastic
Weight Thickness
•Acetone   — — Dissolved
•Cyclohexanone   — — Dissolved
•Di-Isopropyl Ketone   — — Dissolved
•Methyl Ethyl Ketone   — — Dissolved
•Methyl n-Butyl Ketone   — — Dissolved
•Methyl Isobutyl Ketone   — — Dissolved
•Phorone   — — Dissolved
Reagent Time Exposed Percent Increase Observed Condition of Plastic
Weight Thickness
Aluminum Acetate,
Basic, 33%
water slurry		 2 months 1.8 0.6 Unchanged
Aluminum Chloride,
10%		 2 months 1.5 0.7 Unchanged
Aluminum Chloride,
saturated solution		 2 months 0.1 0.0 Unchanged
Aluminum Sulfate,
solid		 3 months 1.7 1.1 Unchanged
Ammonium Bifluoride,
saturated solution		 1 month 2.3 — Slightly bleached
Ammonium Chloride,
saturated solution		 1 month 2.1 0.8 Unchanged
Ammonium Nitrate,
solid		 1 week 0.2 0.2 Unchanged
Ammonium Nitrate,
10%		 1 week 1.7 0.8 Unchanged
Ammonium Sulfate,
solid		 1 year 0.1 0.6 Unchanged
Ammonium Sulfate,
10%		 1 year 1.3 0.5 Unchanged
Calcium Chloride,
2.5%		 1 year 1.5 0.9 Unchanged
Calcium Chloride,
40%		 2 months 0.4 0.0 Unchanged
Calcium Hypochlorite,
6%		 1 year 6.0 –3.8 Softened and cracked
Calcium Hypochlorite,
30%		 13 days 0.8 0.0 Unchanged
Calcium Phosphate,
Monobasic, solid		 1 year 1.7 0.5 Unchanged
Calcium Phosphate,
Dibasic, solid		 1 year –0.6 0.6 Unchanged
Calcium Phosphate,
Tribasic, solid		 1 year –0.6 0.6 Unchanged
Calcium Sulfate
(Gypsum), solid		 1 year –0.1 0.6 Unchanged
Copper Sulfate
(Cupric), 10%		 2 months 1.7 0.6 Unchanged
Copper Sulfate,
saturated solution		 2 months 1.7 0.9 Unchanged
Cuprous Chloride,
solid		 1 week 1.5 — Unchanged
Ferric Ammonium
Sulfate, solid		 1 week
(38ºC, 100ºF, 80% RH)		 0.3 — Unchanged
Ferric Chloride,
5%		 2 months 2.0 0.8 Unchanged
Ferric Chloride,
20%		 2 months 1.7 1.0 Unchanged
Ferric Chloride,
40%		 2 months 1.3 0.4 Unchanged
Ferric Chloride,
saturated solution		 1 month 0.9 0.3 Unchanged
Lithium Bromide,
solid		 1 week –0.7 0.0 Unchanged
Lithium Bromide,
50%		 1 week 0.0 0.0 Unchanged
Magnesium Carbonate,
2.5%		 2 days 1.6 1.0 Unchanged
Potassium Aluminum
Sulfate (alum), 21%		 4 months
(38ºC, 100ºF)		 1.9 0.8 Unchanged
Potassium Bromide,
3%		 3 days
(38ºC, 100ºF)		 1.3 — Unchanged
Potassium Chloride,
solid		 1 year 0.1 0.5 Unchanged
Potassium Chloride,
10%		 1 year 1.7 0.4 Unchanged
Potassium Chrome
Alum, 10%		 3 days
(38ºC, 100ºF)		 1.3 — Unchanged
Potassium Cyanide,
10%		 2 months 1.4 0.3 Slightly discolored (brown)
Potassium Cyanide,
saturated solution		 2 months 0.5 0.0 Slightly discolored (brown)
Potassium
Ferricyanide, 10%		 4 days — — Unchanged
Potassium Sulfate,
solid		 1 year 0.1 0.6 Unchanged
Potassium Sulfate,
10%		 1 year 1.4 0.4 Unchanged
Silver Nitrate,
2.5%		 2 days 1.5 0.0 Unchanged
Sodium Acetate,
3%		 3 days
(38ºC, 100ºF)		 1.3 — Unchanged
Sodium Aluminum
Sulfate, solid		 1 week 1.6 0.4 Unchanged
Sodium Bicarbonate,
2.5%		 2 days 1.7 0.5 Unchanged
Sodium Bisulfate,
solid		 1 week
(38ºC, 100ºF, 80% RH)		 0.1 — Unchanged
Sodium Bisulfate,
1%		 3 days
(38ºC, 100ºF)		 1.3 — Unchanged
Sodium Bisulfite,
20%		 1 week 2.1 0.8 Unchanged
Sodium Borate,
2.5%		 2 days 1.5 0.5 Unchanged
Sodium Carbonate,
solid		 1 week
(38ºC, 100ºF, 80% RH)		 3.9 — Unchanged
Sodium Carbonate,
2.5%		 1 year 1.3 0.9 Unchanged
Sodium Carbonate,
6%		 3 days
(38ºC, 100ºF)		 1.2 — Unchanged
Sodium Carbonate,
10%		 1 year — — Unchanged
Sodium Chloride,
2.5%		 1 year — — Unchanged
Sodium Chloride,
10%		 1 year 1.3 0.5 Unchanged
Sodium Chloride,
saturated solution		 2 months 0.8 0.3 Unchanged
Sodium Chloride,
saturated solution		 2 months
(60ºC, 140ºF)		 0.9 0.9 Unchanged
Sodium Chromate,
saturated solution		 1 week 0.6 0.2 Unchanged
Sodium Cyanide,
10%		 2 months 1.0 0.3 Unchanged
Sodium Cyanide,
saturated solution		 2 months –0.2 –0.4 Unchanged
Sodium
Ferrocyanide,
solid		 1 week 0.8 — Unchanged
Sodium Fluoride,
4%		 1 month 2.5 — Unchanged
Sodium Hypochlorite,
30%		 13 days 1.1 –2.1 Unchanged
Sodium Nitrate,
solid		 2 months 0.1 0.1 Unchanged
Sodium Nitrate,
10%		 1 year 1.2 0.4 Unchanged
Sodium Nitrate,
saturated solution		 2 months 0.9 0.4 Unchanged
Sodium Silicate,
solid		 2 months 0.3 0.2 Unchanged
Sodium Silicate,
saturated solution		 2 months 1.2 0.1 Unchanged
Sodium Sulfite,
10%		 1 week 2.1 0.9 Unchanged
Sodium Thiosulfate,
20%		 13 days 1.1 0.0 Unchanged
Sodium Thiosulfate,
24%		 3 days
(38ºC, 100ºF)		 1.2 — Unchanged
Tetra (2-Ethylbutyl)
Silicate		 1 month
(50ºC, 122ºF)		 –0.7 –0.1 Unchanged
Trimethyl Benzyl
Ammonium
Chloride, 5%		 17 days 1.1 0.1 Unchanged
Zinc Chloride
(hydrous salt)		 1 week 0.5 0.0 Unchanged
Zinc Chloride,
saturated solution		 1 week 1.4 0.8 Slightly etched
Zinc Oxide,
solid		 1 week — — Unchanged



Miscellaneous Chemicals and Gases

Reagent Time Exposed Percent Increase Observed Condition of Plastic
Weight Thickness
 Ammoniated
 Mercury		 1 week (60ºC, 140ºF) — — Unchanged
•Aniline   — — Dissolved
•Benzaldehyde   — — Dissolved
•Butadiene-1,3,
 liquid		 6 months 19.3 26.4 Swollen and softened
 Butadiene-1,3,
 gas		 1 month 2.7 2.3 Unchanged
•Carbon Disulfide 1 week 25.8 1.6 Softened and swollen
•Carbon Disulfide,
 saturated
 atmosphere		 2 days 17.4 11.8 Warped
•Chlorine, dry 1 week 8.8 2.2 Crazed and brittle
•Chlorine, moist 1 week 7.8 0.1 Crazed and brittle
•Chlorine,
 saturated
 solution		 1 week — — Considerably softened and swollen
•1,4-Dioxane   — — Dissolved
 Ethylene Oxide,
 gas		 10 minutes (41ºC, 105ºF) — — Unchanged
•Ethylene Oxide,
 gas		 1 day 20.9 25.6 Swollen and softened
 Formaldehyde,
 4%		 10 min per day for 5 days 0.2 — Unchanged
•Formaldehyde,
 35%		 2 months 13.0 6.7 Swollen and softened
•Furfural   — — Dissolved
 Hydrogen
 Peroxide,
 3%		 1 year 1.7 1.1 Unchanged
 Hydrogen
 Peroxide,
 5%		 2 days 1.4 1.3 Unchanged
 Hydrogen Sulfide,
 dry		 2 months 2.3 0.8 Unchanged
 Hydrogen Sulfide,
 moist		 2 months 3.0 1.7 Unchanged
 Hydrogen Sulfide,
 saturated solution		 2 months 5.9 2.3 Unchanged
 Hydroquinone,
 20 g per gallon		 1 week 2.4 1.0 Slightly stained yellow
•Methyl
 Methacrylate
 Monomer		   — — Dissolved
•Nitrobenzene   — — Dissolved
 Ozone,
 0.05–0.15 ppm		 45 days (outdoors) — — Unchanged
 Ozone, 0.7 ppm 45 days (49ºC, 120ºF) — — Yellowed
•Phenol 1 week — — Decomposed
•Styrene Monomer   — — Dissolved
 Sulfur, solid 1 week — — Unchanged
•Sulfur Dioxide,
 dry		 2 months 19.4 8.6 Swollen, slightly warped
•Sulfur Dioxide,
 moist		 2 months 31.9 10.2 Considerably swollen and warped
•Sulfur Dioxide,
 saturated		 2 months 23.2 18.1 Swollen and warped
•Sulfur Dioxide
 in Hydrocarbons		   — — Dissolved
•Sulfur Dioxide
 and Hydrocarbon
 Vapor		 2 months 19.2 11.5 Swollen
•Titanium
 Tetrachloride		 3 days — — Very brittle
 Trinitrotoluene
 (TNT), water slurry		 4 weeks — — Stained
 

 

 

 

 

 

 

Steel Metal Balls

Tube Caps & Plugs

Springs

Eyebolts

Threaded Rods

Carriage Bolts

Dowel Pins

Lag Screws

Self Drilling Screws

Spring Pins

Drill Bits

Set Screws

Taper Pins

Wood Screws

Sheet Metal Screws

Tapping Screws

Machine Screws

Channels

Felt Discs, Sheets, Strips

 

K-Mac Plastics  3821 Clay Ave. SW, Wyoming, MI  49548

   Contact Kmac Plastics

Privacy

Domestic Selling Policy

Goods and services provided by K-mac Plastics (MI, USA).
Sold by 2CheckOut.com Inc. (Ohio, USA).

Acrylic Pig Show Pipes

Circuit Breakers, UHMW Sheets, Composite Sheets, Pinewood Derby Cars, Steel Plates, Rods, Tubes, Bars, Wooden Puzzle Boards